6061 Aluminium-Band
Modell Legierung: 6061
Temperament: T4, T6, T651, etc
Die Dicke: 0,1 mm-6,5 mm
Breite: 3mm-2600mm
MOQ: 1 Tonne
Lieferung: Fertige Ware: 7-10 Tage, zukünftige Ware: 15-30 Tage
6061 Aluminum Strip Introduction:
6061 aluminum strip contains a lot of magnesium and silicon elements, has excellent processing performance, medium strength, is an alloy that can be strengthened by heat treatment, and can still maintain good operability after annealing. Widely used in industrial structural components, showing good corrosion resistance and weldability.
Parameters of 6061 Aluminum Strip:
Verarbeitung und Umformung | 6061 aluminum can be cut, machined, bent, welded, rolled, deep drawn and other processing processes. |
Oberflächenbehandlung | Mill finish、coated、powder coated、anodized、polished mirror、embossed、etc. |
Toleranzen | Je nach Anforderung des Kunden |
Hafen laden | Hafen Qingdao, Hafen Tianjin, Hafen Shanghai. |
Preisbedingungen | FOB, CIF, CFR, CNF, usw. |
Zahlungsbedingungen | L/C, D/A, D/P, T/T, West Union, Money Gram, Etc. |
Normen | ASTM-B209,EN573-1,GB/T3880.1-2006 |
Zertifikat | ISO, RoHS |
Schweißen | Konventionelles Argonlichtbogenschweißen, Widerstandspunktschweißen, Laserschweißen und andere Schweißverfahren. |
Wärmebehandlung | Lösungsbehandlung und Alterungsbehandlung. |
Schmieden | Warmumformung, Kaltumformung, etc. |
Heat Treatment Process:
1. Rapid annealing: heating temperature 350~410℃; depending on the effective thickness of the material, the holding time is between 30~120min; air or water cooling.
2. High temperature annealing: heating temperature 350~500℃; when the thickness of the finished product is ≥6mm, the holding time is 10~30min; when it is less than 6mm, the heat preservation time is until it is heated through; air cooling.
3. Low temperature annealing: heating temperature 150~250℃; holding time 2~3h; air or water cooling.
4. Homogenization: 570 degrees Celsius, heat preservation for 7 hours; air cooling.
6061 Aluminum Specification:
Chemische Zusammensetzung:
Legierung |
Si | Fe | Cu | Mg | Mn | Cr | Zn | Ti | Ni | Zr |
Al |
6061 | 0.3-0.7 | 0.5 | 0.1 | 0.35-0.8 | 0.03 | 0.03 | 0.1 | – | – | – |
Bleiben Sie |
Mechanical Properties:
- Tensile Strength: 310 MPa – 415 MPa
- Yield Strength: 276 MPa – 310 MPa
- Elongation: 12% – 16%
Physical Properties:
Klasse | 6061 |
Dichte | 2,70 g/cm³ |
Schmelzpunkt | 582 °C |
Elastischer Modul | 69 GPa |
Wärmeleitfähigkeit | 167 W/(m·K) |
Elektrische Leitfähigkeit | 43.9 MS/m |
Spezifische Wärmekapazität | 897 J/(kg·°C) |
Advantages of 6061 Aluminum Strip:
- Hohe Festigkeit.
- Solderability.
- High corrosion resistance.
- Verarbeitbar.
- Gute Wärmeleitfähigkeit.
- Anti-Müdigkeit.
- Leicht zu färben.
- Verformbar.
Produkt- und Verpackungsfotos
Warum uns wählen
Yongsheng Aluminum ist ein führender Hersteller und Lieferant von Aluminiumprodukten in China mit 25 Jahren Exporterfahrung. Unsere hervorragende Produktqualität, unser Preis und unsere stets pünktliche Lieferung haben uns viele langfristige Partner eingebracht und uns weltweit einen guten Ruf eingebracht. Wir bieten Produktlösungen aus einer Hand für CC&DC Aluminiumprodukte.